Solids-containing, water-absorbing anionic polymers having a sponge structure and the production and use thereof

ABSTRACT

The invention is directed to a crumbly, water-absorbing, soil-like hydrogel. The hydrogel comprises finely comminuted mineral substances, such as igneous rock; water-soluble alkali-silicate; solid and liquid nutrient additives; and ballast, bound in a cross-linked polymer. The hydrogel is structured like a sponge and absorbs water and liquids when in contact with water or aqueous liquids. The mineral substances present in the hydrogel may be present in an amount of at least 30% by weight of the dried hydrogel. Also, the invention encompasses methods of producing acidic and neutral to weakly alkaline hydrogels.

[0001] The invention relates to a crumbly, water absorbing, soil-like product consisting of finely comminuted mineral substances, preferably igneous rock, and water-soluble alkali-silicate and possibly further solid and liquid additives as nutrients, helpful substances and ballasts, bound in a cross-linked polymer that is structured like a sponge and forms in contact with water or aqueous liquids hydrogel. The amount of mineral substances in the product is at least 30%-wt. (referring to a dried product). The invention provides two production-methods for manufacturing of acidic and neutral to weakly alkaline products.

[0002] Due to the manner of production and composition the new product is different from conventional materials, the appearance is topsoil-like and comparable to humus in undried or rewetted condition. Water-absorption is not alone a function of hydrogel-swelling but also a part of pore-capacity that enlarges during swelling.

[0003] Water and aqueous liquids absorbing polymers forming hydrogels are described already often before. The production is realized with unsaturated, water-soluble acid groups containing monomers (as acrylic acid or derivatives thereof), mostly after partial neutralisation of the acid groups with alkaline, together with one or several cross-linking agents having at least two olefinically unsaturated groups in the molecule. In one way the polymerisation runs in aqueous solutions or in the other way according to the process of inverse suspension- or emulsion-polymerisation as described in U.S. Pat. No. 4,286,082, DE-PS 27 06 135, U.S. Pat. No. 4,340,706, DE-PS 28 40 010.

[0004] Further possibilities are given according to the production of graft-polymers by use of modified starch and cellulose (DE-OS 26 12 846) or polyvinylalcohol (DE-PS 40 20 780) and the subsequent treatment of the polymer-gel-particles or the powdery resin by cross-linking on the surface, as described in DE-PS 40 20 780 C1.

[0005] As comonomers are used water-soluble mono-ethylenic, unsaturated monomers as acidamides, preferably acrylamide, methacrylamide, N-alkylene (meth)-acrylamide, N-dialkylene amino-alkylene(meth)-acrylamide, N-dialkylene amino-alkylene (meth)acrylamide, N-methylol-(meth-) acrylamide and N-vinyl-amide as N-vinylformamide, N-vinyl-acetamide and N-vinyl-N-methyl-acetamide, N-vinyl-N-methyl-formamide and further vinyl-pyrrolidone as well as hydroxyalkylene-(meth-)acrylate for example hydroxy-ethyl-acrylate and (meth-)acrylic acid-ester of polyethylene-glycol-mono-allylether and allylether of polyethylene-glycols.

[0006] A favourable production method according to EP 205 674 A1 is also the polymerisation of an unneutralized, aqueous monomer-solution within a temperature of 0 to 100° C., preferably 5 to 40° C., and subsequently, when forming and shredding of the hydrogel is done, a forced neutralisation with an alkaline solution in an extruder.

[0007] All of these polymers received by different methods are amply known as “superabsorbers”.

[0008] Favourite fields of use for these products are hygienic and sanitary applications. To meet the requirements these superabsorbers must have skin-neutrality and the property of rapid and complete absorption of secretion. These hydrogels are therefore neutralized to an extent of 50 to 80 mol-%, relating to acid-groups in the polymer. A higher velocity for absorption can be received by heat treatment of dried and shredded polymer-particles in presence of a after-cross-linking-agent (DE-PS 40 20 780 C1).

[0009] It was obvious, also to use hydrogel-forming polymers in the botanical field for water-storing. But the transfer failed because of the different requirements.

[0010] To obtain a good growing of plants the whole structure of soil in combination with superabsorbers had to be considered. Characteristics as climate and capillarity of soil are just as important as water-capacity before.

[0011] Supply and demand of minerals and nutrients had also to be seen and integrated into the calculations. Besides that it turned out that the polymers were very sensitive to basic earth and UV-light. As written in application DE-Appl. 101 14 169,6 these last-named deficiencies of superabsorbers can be overcome by adding of alkali-silicate. The task was therefore now to combine all these recognitions in a new robust porous polymer- and solids-containing material, that is air-permeable, water-absorbing and nevertheless a optimal source for nutrients.

[0012] It must also be emphasized, that there is no tendency to float, when the soil is too wet, because of the weight of the solids-containing polymer.

[0013] The properties of the new product can be varied in wide limits by changing the polymer-bounded solid minerals in relation to type and quantity. However, comminuted igneous rock as mineral nutrient is preferably and/or predominantly included in. This rock is splitted into two groups according to its SiO₂-content. The first group, here named “A” and “basic” has a SiO₂-content less than 50%-wt. the second one, here named “B” and “acid”, has at least 50%-wt. Because the manufactured product should be generally neutral, comminuted rock of group A is preferably used. This is done not at least to spare with alkali in this way. The second group of rock is then opportune, when the manufactured product shall be used for absorption of aqueous basic liquids and/or ammonia and for treatment of substances arising from bacterial decomposition of organic materials as liquid manure.

[0014] It must be mentioned, that the anorganic contents of igneous rock, especially trace elements in dependence on particle-sizes, is influencing the course of polymerisation and consequently the structure of the sponge. Therefore, it is necessary, to check up the influence of comminuted rock, which is present.

[0015] The particles of the comminuted rock, bound in the polymer, what is for the plants a source of mineral nutrient, should be less than 200 μm, preferably less than 100 μm in view of the diameter.

[0016] The additional solid minerals, which are secondary to the igneous rock and are not absolutely necessary, have an influence on the production process and the application in different ways. Suitable minerals subdivided into their functions shows the following table (3 sorts):

[0017] a) Acid-sensitive, helpful minerals as carbondioxid-suppliers for inertisation of the monomer-solution, for instance chalk, trass, dolomite and magnesite.

[0018] b) Minerals as solution-thickeners, sponge-stabilizers, cation-catchers, polymerisation-inhibitors and swelling-accelerators.

[0019] c) Ballasts and fillers from natural components of the top-earth: feldspar and quartz sand are named.

[0020] It is usual to remove oxygen from the monomer-solution before beginning the polymerisation. Mostly nitrogen is introduced for a longer time. It was found out, that carbonate containing minerals are producing enough carbondioxid under the present conditions to manage the polymerisation and to get a robust and homogeneous structure of the sponge (sort a). An alternative method is to introduce gaseous carbondioxid or soda water.

[0021] Minerals of sort b) as bentonite have the property to absorb small amounts of aqueous liquids by themselves and act as cation-catchers. Therefore, they make a contribution to the strength and the swelling of the sponge. But(it must be also remarked, that) they have an inhibiting effect on polymerisation. Their particle-size should be between 0,1 and 8,0 mm, preferably between 0,3 and 5,0 mm in view of diameter.

[0022] Though minerals of sort c) have no special functions for the manufacture of the product they are nevertheless be listed. They are counted to the solid mineral-content of the product and are influencing his weight. Therefore they must be mentioned. There are no special requirements for these ballast-substances except that their particle-size should be similar to sort b).

[0023] The solid mineral-content of the inventive product is at least 30%-wt., referring to a dried substance. This includes igneous rock of groups “A” and “B” and the solid minerals of sorts a), b) and c).

[0024] The rest of the components, which are necessary for the production, are neutalizing agents and alkali-silicate. Also, can be added K-, N-, P- and Si-containing fertilicers, if wished.

[0025] It was recognized by carrying out of the polymerisation, that the homogeneously mixed solid minerals in the monomer-solution can agglomerate and flocculate during the process and act very destructive. That was the reason to seek a polymerisation-process, which is simple to manage and where no disturbing reactions occur. This task was solved by two ways, which take into account the determined extent of neutralisation.

[0026] Production Method I:

[0027] The minerals and the unpolymerizable, water-soluble components are introduced into alkalisilicate-, alkalicarbonate- and/or carbondioxide-containing water, what additionally may comprise an oxidising catalyst to avoid agglomeration. Subsequently are added the water-soluble, olefinically unsaturated acid groups containing monomers together with the cross-linking agent and with the comonomers as well, if provided. After end of foaming (formation of carbondioxide) the polymerisation is carried out. Then the product can be cutted or shredded.

[0028] There is no further treatment necessary, if the product is planned for absorption of alkaline liquids or ammonia or if the amount of basic igneous rock of group “A” was enough to reach an unsensitive pH-value to plants. Otherwise it is possible to neutralize a surplus of acid by basic earth and/or alkalihydroxide or by mixing the cutted or shredded product with chalk or dolomit.

[0029] Production Method II:

[0030] The minerals and the unpolymerizable, water-soluble components are introduced into alkalisilicate-, alkalihydroxide-, alkalicarbonate- and/or carbondioxide-containing water, where the amount of alkaline is 40 mol %-in maximum (referring to the sum of acid groups containing monomers), what in addition may comprise an oxidising catalyst to avoid agglomeration. The exceeding alkaline amount, which is necessary to reach neutrality, is filled into a hydrophilic and/or porous solid mineral. To prevent a reaction with acid groups too soon it is capsulated, for instance with wax. Subsequently are added the water-soluble, olefinically unsaturated acid groups containing monomers together with the crosslinking agent and with the comonomers as well if provided. After end of foaming (formation of carbondioxide) the polymerisation is carried out. The rest is as above.

[0031] In this way are manufactured any acidic to weakly neutral or weakly alkaline products with robust sponge-structures, which are able to absorb water nearly similar to superabsorbers in dependence to the pH-value. The amount of water is allocated to the pore- and gel-capacity. When mixed with soil, rains and droughts are causing increases and decreases of the mass, what makes a breathing of the soil. Because of the mineral content of the product the quality and the climate of the soil are improved.

[0032] After manufacture and shredding of the product numerous pockets offer the opportunity to insert solids of varying particle-sizes and bulk-weights without fearing separations during storing or transport. The solids can be minerals of this inventive polymer, but also organic substances of natural or synthetic origin, here named as group “N” (no mineral). Counted to this group are for instance algae, bast, brown coal, hemp, wood, wholemeal of ricinus, hard coal, straw, peat and water-insoluble as well as water-swelling polymers. The subsequent insertion of diverse materials opens applications, which have no concern with the agricultural sector. These will be noticed later. The pockets are opened and closed by changing the water-content of the product.

[0033] As already explained above, superabsorbers are water absorbing polymers on basis of homo- and copolymers of olefinically unsaturated carbonacids. Exemplary are named: acrylic acid, maleinic acid, fumaric acid, itaconic acid, vinyl-sulfonic-acid as well as acrylamido- and methacrylamido-alkyl-sulfonic-acid as acrylamido-2-methylpropane-sulfonic-acid, 2-methylacryloyl-oxiethane-sulfonic-acid, 4-vinyl-benzene-sulfonic-acid, allyl-sulfonic-acid, vinyl-toluene-sulfonic-acid, vinyl-phosphonic-acid and vinyl-benzenephosphonic-acid, but preferably acrylic acid, meth-acrylic acid and/or maleinic acid.

[0034] As water-soluble, copolymerizable, olefinically unsaturated monomers are suitable substances, which are already summed up above, therefore they need no repetition. The comonomers can amount up to 50%-wt., referring to the polymerizable components of the monomer-mixture. As water-soluble additional polymers can be used: homo- and copolymers of the monomers named before, partly saponificated polyvinylacetate, polyvinylalcohol, starch, starch-derivates, grafted starch, cellulose and cellulose-derivates as carboxi-methyl-cellulose and galactomannose as well as the oxalkylated derivates.

[0035] The aqueous monomer-solution contains at least one cross-linking agent amounting 0,01-5,0%-wt., preferably 0,1-2,0%-wt., relative to the sum of polymerizable monomers. As cross-linking agents are suitable all substances having at least two olefinically, unsaturated groups or at least one olefinically unsaturated group, which is reactive against acid groups. Representatives are methylenbisacrylamide, mono-, di- and polyesters of acrylic acid, methacrylic acid, itaconic acid and maleinic acid of alcohols with more than one hydroxy-group as 1,4-butandiol, 1,6-hexandiol, polyethyleneglycol, trimethylolpropane, pentaerythrite, glycerine, polyglycerine as well as substances, which are deriving thereof by oxalkylation. Further are named: diallylacrylamide, diallylphthalate, triallylcitrate, trimonoallyl-polyethylene-glycolether-citrate and allylether of di- and polyols just as oxethylates thereof. Representatives of the last group are polyallylether of glycerine, trimethylolpropane, pentaerythrite and oxethylates thereof. Tetraallyloxiethane, polyglycidylallylether as well as ethylenglycol-glycidether and glycerine-glycidylether belong to this type too. Finally shall be mentioned amines and the salts thereof with at least two olefinically unsaturated substitutes: these are di- and triallylamin and tetraallylammoniumchloride.

[0036] The radical polymerisation is initiated by usual redox-systems: peroxo- and azo-substances as potassium-peroxo-monosulfate, potassium-peroxodisulfate, tert.-butyl-hydroperoxide, 2,2′-azo-bis(2-methylen-propionamidine)-dihydrochloride and hydroperoxide together with one or more reducing agents as potassiumsulfite, potassiumformamidinesulfinate and ascorbic-acid. Normally the oxidising agent is introduced first. In the operational praxis the initiation is preferably effected by photocatalysis and sensibilisators.

[0037] After the manufacture the product is obtained in blocks. Therefore a comminution is necessary for instance by shredding. Often the first step is slicing to get mats. From there many different forms are available well suited to the application. Square sticks are desirable, when the plants need during a later period of growth further amounts of minerals and nutrients. A top-soil like, crumbly product similar-looking as humus is got by shredding. In fresh condition the product is a little bit sticky. This property can be used, to produce many various forms and constructions by squeezing together crumbs.

[0038] The product is suitable for germination, growth and cultivation of plants. Best results are to expect, when the product is mixed up with soil, also with unfavouable soil and exposure to bad weather. By the way the product permits an economizing of irrigation and is therefore especially helpful in rainless cultivation zones. It is possible to use the inventive product alone for raising of plants. A special form of application is the use in plant buckets, which are combined by capillar poles with a water-reservoir, from which the crumbly product-sponges catch water and fertilizer, what is taken by the roots.

[0039] The crumbs with their pores and pockets can be carriers for numerous different solids. From the many possibilities of combination is specially named the filling with wholemeal of ricinus. Wholemeal of ricinus is obtained at the winning of ricinusoil and is counted to the group of solid fertilizers.

[0040] A further possibility is a mixture of a fertilizer-free product with woodmeal or sawdust, which is subsequently dried. This can be used as straw for animals like cats and dogs.

[0041] Of interest could be, to fill the crumbs subsequently with finest, often dusty synthetic polymer particles, whose application in pure form is normally very problematic. Because of the slight stickiness of the fresh crumbs also fabrics and fleeces can be equipped with and that without drizzling. The objects are there useful, where locked water-absorbing products with a stock of minerals and nutrients are required. This is the cultivation of slopes. Other areas of application are enclosures for goods for sale and for coffins (cascets).

[0042] Are these crumbs-containing fabrics and fleeces additionally equipped with natural and synthetic material, that is light enough to float, then these objects can be used in moist areas for plant-raising as rice and together with insecticides for controlling of insects.

[0043] These examples show that the inventive product with his extraordinary property and his pocket-structure is both a carrier for synergy as well as something for different solid and liquid substances.

EXAMPLES

[0044] The following solids are used:

[0045] a) Eifellava: Eifelgold-Urgesteinsmehl, FA. LAVA-UNION GmbH, D-53489 Sinzig,

[0046] b) Trass: Fa. Marker-Zementwerk GmbH, D-86665 Harburg,

[0047] c) Bentonit: Smektonit Agrarbentonit 0/8, Fa. MARX Bergbau GmbH & Co. D-5431 Ruppach-Goldhausen.

[0048] The chemicals were supplied by Fa Merck Eurolab GmbH, D-44866 Bochum. Fa. Wako Chemicals GmbH, Neuss: Wako V-50.

[0049] Suppliers for the solids were:

[0050] Fa. Baerle & Co, D-76593 Gemsbach/Rhein: potassium-silicate (Kaliwasserglas, type 28-30° Bé)

[0051] Fa. Henkel KGaA, D-40191 Dusseldorf: potassium-silicate, type 28-30° Bé.

Example 1

[0052] 40,0 g Eifelgold, 15,0 g Trass and 15,0 g Bentonit are finely stirred into 40,0 g soft soda water. Then is poured in unter stirring in portions a solution, consisting of 15,0 g acrylamide, 35,0 g acrylic acid, 160 mg 1,4-butandioldiacrylate and 30,0 g soft water, that the foaming can be controlled. After the end of foaming the polymerisation is initiated by adding of the following catalysts in the named order: 1 ml aqueous solution of Wako-V 50 (1,0%-wt.), 2,0 ml aqueous solution of sodiumperoxidisulfate (1,0%-wt.), 1 ml aqueous solution of ascorbic acid (0,2%-wt.) and 1 ml aqueous solution of potassiumdisulfite (1,25%-wt.). It is produced a robust block with many internal pores that it has the appearance of a sponge. Some minutes later the block can be sliced. The absorption of this product is only minimal, because the acid groups of the polymer are not neutralized. On the other hand, when a slice is put into tapwater (20° dH), containing 15,0 g potassium-hydroxide and 3,0 g potassium-silicate (50%), a 30-fold increase of the weight is received after 24 hours.

Example 2

[0053] 40,0 g Eifelgold, 15,0 g Trass and 15,0 g Bentonit are finely stirred into 70,0 g soft soda water. Then is poured in under stirring in portions 5,0 g potassiumsilicate (50%-wt.) and a mixture, consisting of 50,0 g acrylic acid and 160 mg 1,4-butandioldiacrylate, that the foaming can be controlled. After the end of foaming the polymerisation is initiated analogous example 1. When a slice is put into tapwater (20° dH), containing 21,5 g potassium-hydroxide, nearly a 40-fold increase of the weight is received after 24 hours.

Example 3

[0054] 20,0 g Eifelgold and 5,0 g Bentonit are finely stirred into 70,0 g soft soda water. Then is poured in under stirring in portions 5,0 g potassiumsilicate (50%-wt.) and a mixture, consisting of 50,0 g acrylic acid and 160 mg 1,4-butandioldiacrylate, that the foaming can be controlled. After the end of foaming the polymerisation is initiated analogous example 1. When a slice is put into tapwater (20° dH), containing 21,5 g potassium-hydroxide, nearly a 60-fold increase of the weight is received after 24 hours.

Example 4

[0055] 115,0 g Eifelgold, 15,0 g Trass and 20,0 g Bentonit are finely stirred into 64,0 g soft soda water, containing 12,0 g potassiumsilicate (50%-wt.), 14,0 g potassiumhydroxide, 2,0 g urea and 1,5 g phosphoric acid (50%-wt.).Then are introduced 2,0 ml of an aqueous solution of sodiumperoxidisulfate (1,0%-wt.). Subsequently is poured in under stirring in portions a mixture, consisting of 50,0 g acrylic acid and 200 mg 1,4-butandioldiacrylate, that the foaming can be controlled. After the end of foaming the polymerisation is initiated analogous example 1. When a slice is put into tapwater (20° dH), nearly a 20-fold increase of the weight is received after 24 hours.

Example 5

[0056] 100,0 g Eifelgold, 15,0 g Trass and 40,0 g of a mixture Bentonit/expanded clay (1:1, containing additionally 10,0 g of potassiumhydoxide-solution-50% and 12,0 g potassiumsilicate, locked by capsulation with wax) are finely stirred into 64,0 g soft soda water, containing 2,0 g urea, 1,5 g phosphoric acid (40%-wt.) and 14,0 g potassiumhydroxide. Then are introduced 2,0 ml of an aqueous solution of sodiumperoxidisulfate (1,0%-wt.). Subsequently is poured in under stirring in portions a mixture, consisting of 50,0 g acrylic acid and 200 mg 1,4-butandioldiacrylate, that the foaming can be controlled. After the end of foaming the polymerisation is initiated analogous example 1. When a slice is put into tapwater (20° dH), nearly a 28-fold increase of the weight is received after 24 hours.

Example 6

[0057] An amount of 100 g crumbs, taken from an production analogous example 4 and subsequently shredded, was mixed up with 15,0 g calciumcarbonate, partially dried and then used as plant-substratum for barley with good results.

Example 7

[0058] An amount of 100 g crumbs, taken from an production analogous example 4 and subsequently shredded, was mixed up with 100 g sawdust, partially dried and then used as cat-toilet.

Example 8

[0059] An amount of 100 g crumbs, taken from an production analogous example 4 and subsequently shredded, was mixed up with 100 g wholemeal of ricinus, partially dries and then used in window-boxes. 

1. A crumbly, water absorbing, soil-like product, consisting of water-soluble alkali silicate and finely comminuted mineral substances, preferably igneous rock and possibly further solid and liquid additives, bound in a crosslinked polymer, that is structured like a sponge and forms hydrogel with water and aqueous liquids. The amount of mineral substances in the product is at least 30%-wt. (referring to a dried product).
 2. A product according to claim 1 where in the mineral substances represent following classes: Class 1: a) Basic igneous rock, containing less than 50%-wt. SiO₂ (arithmetically). b) Acid igneous rock, containing at least 50%-wt. SiO₂ (arithmetically). Class 2: a) Substances, produced by the reaction of acid monomers with carbonates to get carbondioxide for displacing oxygen from the reaction mixture. Carbonates may be chalk, dolomites, trass and magnesite. b) Thickeners, sponge-stabilizers, cation-catchers, polymerisation-inhibitors and swelling-promoters. A multifunctional substance is water-absorbing clay as bentonite. Class 3: a) Minerals as feldspar or quartz-sand. b) Further solid natural and synthetic substances as: Algae, bast, brown coal, hemp, wood, wholemeal of ricinus, hard coal, straw, peat and water-soluble polymers.
 3. A product according to claim 1 and 2 where in the crosslinking polymer is formed of: a) 55-99%-wt. of at least one unsaturated, polymerizable, acid groups containing monomer, b) 0-40%-wt. of unsaturated monomers, which are copolymerizable with the monomer according to 3a), c) 0,01-5,0%-wt. of at least one crosslinking agent and d) 0-30%-wt. of a water-soluble polymer.
 4. A product according to claims 1-3 where in the water-soluble alkalisilicate is sodium- or potassium-silicate as it is formed by alkaline melting of quartz-sand.
 5. A product according to claims 1-4 where in at least one solid or liquid representative out of K-, N-, P- and Si-containing fertilizers is additionally included.
 6. A product according to claims 1-5 where in the water-soluble, unsaturated, polymerizable acid groups containing monomer is acrylic acid, maleinic acid, fumaric acid, itaconic acid, vinyl- sulfonic-acid as well as acrylamido- and methacrylamidoalkyl-sulfonic-acid as acrylamido-2-methylpropane-sulfonic-acid, 2-methylacryloyl-oxiethane-sulfonic-acid, 4-vinyl-benzene-sulfonic-acid, allyl-sulfonic-acid, vinyltoluene-sulfonic-acid, vinyl-phosphonic-acid and vinyl-benzene-phosphonic-acid, but preferably acrylic acid, meth-acrylic acid and/or maleinic acid.
 7. A product according to claims 1-6 where in the water-soluble, unsaturated monomers, which are copolymerizable are acidamides, preferably acrylamide, methacrylamide, N-alkylene(meth)-acrylamide, N-dialkyleneamino-alkylene(meth)acrylamide, N-dialkyleneamino-alkylene(meth)-acrylamide, N-methylol-(meth)acrylamide and N-vinyl-amide as N-vinylformamide, N-vinyl-acetamide and N-vinyl-N-methyl-acetamide, N-vinyl-N-methyl-formamide and further vinyl-pyrrolidone as well as hydroxialkylene-(meth-)acrylate for example hydroxi-ethyl-acrylate and (meth-)acrylic acid-ester of polyethylene-glykol-mono-allyl-ether and allylether of polyethylene-glykols.
 8. A product according to claims 1-7 where in the polymerized, acid groups containing monomers are preferably and/or predominantly potassium-salts.
 9. A product according to claims 1-8 where in the minerals according to claims 1 and 2 is lava with a particle size less than 200 μm, preferably less than 100 μm.
 10. Process for manufacturing of the product according to claims 1-9 where in first of all the comminuted mineral substances are submitted together with the non-polymerizable components and the alkaline-earth-carbonates, but preferably alkalicarbonates or simply carbondioxide in water as a slurry, which additionally may contain an oxydizing catalyst to avoid clumping together of the solid minerals, afterwards the acid (acid groups containing monomer) together with the crosslinking agent and, if wished, with further comonomers is added to the slurry by stirring. Reaction occurs by releasing of carbondioxide and building of foam. When foaming is nearly over, the polymerisation is initiated. After hardening of the substance the product is cutted and shredded.
 11. Process for manufacturing of the product according to claims 10, where in the slurry contains acid-neutralizing alkaline-earth- and alkalisubstances, preferably alkalihydoxide, alkalicarbonate and alkalisilicate in an amount which doesn't exceed 40%-mol of the acids referring to the acid containing monomers and optionally a further amount capsulated in hydrophilic and/or porous solid substances.
 12. Application of the product according to claims 1-9 with a degree of neutralization of 0-40%-mol for absorption of aqueous basic liquids and/or ammonia and for treatment of substances arising from bacterial decomposition of organic materials as liquid manure.
 13. Application of the product according to claim 1-9 in agriculture for water-storage and supplier for nutrients to sprouts and cultivation of plants either without or with addition of soil.
 14. Application of the product according to claim 1-9 as carrier for solid and liquid fertilizers.
 15. Application of the product according to claim 1-9 embedded in natural and/or synthetic flat fiber-con structures as mats or fleeces for cultivation of slopes.
 16. Application of the product according to claim 1-9 for cultivation of plants on roofs.
 17. Application of the product according to claim 1-9 embedded in natural and/or synthetic flat fiber-constructures as mats or fleeces together with lightweight natural or synthetic materials for cultivation of plants as rice in moist areas in completely or partly flooded regions.
 18. Application of the product according to claim 1-9 as carrier for insecticides, pestizides, bacterizides and fungicides.
 19. Application of the product according to claim 1-9 as carrier for dusty, fine-grained mineral, biologic-natural and/or synthetic solids.
 20. Application of the product according to claim 1-9 for manufacture of dust collectors. 